Duromineral®
Molybdate Orange - standard quality
| Properties |
Duromineral Orange
2147
AT
|
| Lead content
± 1 % |
61 %
|
| Chrome VI content ±
1 % |
12.7 % |
| Density |
5.6 g/ml |
| Apparent density |
0.55 kg/l |
| Oil absorption ± 10 % |
20 g/100 g |
| Fineness |
max. 45 µm
|
| Hiding power, TiO2
= 100 % |
160 % |
| Lightfastness
masstone/tint 1:10 TiO2 |
6-7/7
|
|
Temperature resistance (30 min.) |
180 ° C |
| Fastness to acids/alkalis |
4/2
|
Duromineral®
Molybdate Orange - highly stabilized
excellent light- and weatherfastness
and improved heat stability
| Properties |
Duromineral Orange
3147 AT
|
Duromineral Orange
3527 AT
|
| Lead content
± 1 % |
61 %
|
61 %
|
| Chrome VI content ±
1 % |
12.6 % |
12.3 % |
| Density |
5.6 g/ml |
5.6 g/ml |
| Apparent density |
0.55 kg/l |
0.45 kg/l |
| Oil absorption ± 10 % |
25 g/100 g |
20 g/100 g |
| Fineness |
max. 45 µm
|
max. 45 µm
|
| Hiding power, TiO2
= 100 % |
160 % |
160 % |
| Lightfastness
masstone/tint 1:10 TiO2 |
7-8/8
|
7-8/8
|
|
Temperature resistance (30 min.) |
180 ° C |
180 ° C |
| Fastness to acids/alkalis |
4/2
|
4/2
|
| Properties |
Duromineral Orange
5191
AT
|
| Lead content
± 1 % |
61 %
|
| Chrome VI content ±
1 % |
12.4 % |
| Density |
5.6 g/ml |
| Apparent density |
0.55 kg/l |
| Oil absorption ± 10 % |
20 g/100 g |
| Fineness |
max. 45 µm
|
| Hiding power, TiO2
= 100 % |
160 % |
| Lightfastness
masstone/tint 1:10 TiO2 |
7-8/8
|
|
Temperature resistance (30 min.) |
180 ° C |
| Fastness to acids/alkalis |
4/2
|
| Properties |
Duromineral®
Molybdate Orange
|
| Colour Index |
P.R. 104 |
| Chemical formula |
Pbx(Cr, S; Mo)O4y |
| soluble lead (ISO
3710, 3711) |
< 5 % |
| pH-value |
6.5 - 7.5 |
| Conductivity |
max. 700 µS cm-1 |
| Moisture |
max. 1.5 % |
| Coloristic |
max. dE = 1.5 |
| Colour Strength |
max. ± 5 % |
|
Fastness to solvents |
5 |
|
Fastness to cement/lime |
no/no |
| Storage
conditions |
indoor, dry |
| Storage stability |
at least 5 years if stored properly |
|
Applications |
Duromineral®
Molybdate Orange |
|
standard quality |
highly stabilized |
|
in paints and lacquers: |
|
|
| Oil
and resin finishes |
+ |
+ |
|
baking finishes* |
+ |
+ |
|
NC lacquers |
+ |
+ |
|
Acrylics |
+ |
+ |
|
Epoxide finishes |
O |
O |
|
Polyurethane finishes |
O |
O |
|
Polyester finishes |
+ |
+ |
|
Powder coating |
- |
+ |
|
water soluble finishes |
+ |
+ |
|
Dispersion paints |
+ |
+ |
|
in plastics: |
|
|
|
LD-Polyethylene |
O |
+ |
|
HD-Polyethylene |
O |
O |
|
Polypropylene |
+ |
+ |
|
Flexible-/rigid-PVC |
+ |
+ |
|
Polystyrene |
+ |
+ |
| ABS* |
- |
O |
| PET |
O |
O |
| PBT/PC/PA |
- |
O |
|
Polyurethane |
+ |
+ |
* temperature resistance of the pigment has to be